Extreme ultraviolet lithography
Extreme ultraviolet lithography (EUVL, also known simply as EUV) is a new technology used in the semiconductor industry for manufacturing integrated circuits (ICs). It is a type of photolithography that uses extreme ultraviolet (EUV) light to create intricate patterns on silicon wafers.
As of 2023[update], ASML Holding is the only company that produces and sells EUV systems for chip production, targeting 5 nanometer (nm) and 3 nm process nodes.
The EUV wavelengths that are used in EUVL are near 13.5 nanometers (nm), using a laser-pulsed tin (Sn) droplet plasma (Sn ions in the ionic states from Sn IX to Sn XIV give photon emission spectral peaks around 13.5 nm from 4p64dn – 4p54dn+1 + 4dn−14f ionic state transitions.[1]), to produce a pattern by using a reflective photomask to expose a substrate covered by photoresist.
![](http://up.wiki.x.io/wikipedia/commons/thumb/c/cd/EUV_photoelectrons_and_secondaries_%28vector%29.svg/350px-EUV_photoelectrons_and_secondaries_%28vector%29.svg.png)
History and economic impact
[edit]In the 1960s, visible light was used for the production of integrated circuits, with wavelengths as small as 435 nm (mercury "g line").
Later, ultraviolet (UV) light was used, at first with a wavelength of 365 nm (mercury "i line"), then with excimer wavelengths, first of 248 nm (krypton fluoride laser), then 193 nm (argon fluoride laser), which was called deep UV.
The next step, going even smaller, was called extreme UV, or EUV. The EUV technology was considered impossible by many.
EUV light is absorbed by glass and air, so instead of using lenses to focus the beams of light as done previously, mirrors in vacuum would be needed. A reliable production of EUV was also problematic. Then, leading producers of steppers Canon and Nikon stopped development, and some predicted the end of Moore's law.[citation needed]
In 1991, scientists at Bell Labs published a paper demonstrating the possibility of using a wavelength of 13.8 nm for the so-called soft X-ray projection lithography.[2]
To address the challenge of EUV lithography, researchers at Lawrence Livermore National Laboratory, Lawrence Berkeley National Laboratory, and Sandia National Laboratories were funded in the 1990s to perform basic research into the technical obstacles. The results of this successful effort were disseminated via a public/private partnership Cooperative R&D Agreement (CRADA) with the invention and rights wholly owned by the US government, but licensed and distributed under approval by DOE and Congress.[3] The CRADA consisted of a consortium of private companies and the Labs, manifested as an entity called the Extreme Ultraviolet Limited Liability Company (EUV LLC).[4]
Intel, Canon, and Nikon (leaders in the field at the time), as well as the Dutch company ASML and Silicon Valley Group (SVG) all sought licensing. Congress denied[citation needed] the Japanese companies the necessary permission, as they were perceived[by whom?] as strong technical competitors at the time and should not benefit from taxpayer-funded research at the expense of American companies.[5] In 2001 SVG was acquired by ASML, leaving ASML as the sole benefactor of the critical technology.[6]
By 2018, ASML succeeded in deploying the intellectual property from the EUV-LLC after several decades of developmental research, with incorporation of European-funded EUCLIDES (Extreme UV Concept Lithography Development System) and long-standing partner German optics manufacturer ZEISS and synchrotron light source supplier Oxford Instruments. This led MIT Technology Review to name it "the machine that saved Moore's law".[7] The first prototype in 2006 produced one wafer in 23 hours. As of 2022, a scanner produces up to 200 wafers per hour. The scanner uses Zeiss optics, which that company calls "the most precise mirrors in the world", produced by locating imperfections and then knocking off individual molecules with techniques such as ion beam figuring.[8]
This made the once small company ASML the world leader in the production of scanners and monopolist in this cutting-edge technology and resulted in a record turnover of 18.6 billion euros in 2021, dwarfing their competitors Canon and Nikon, who were denied IP access. Because it is such a key technology for development in many fields, the United States licenser pressured Dutch authorities to not sell these machines to China. ASML has followed the guidelines of Dutch export controls and until further notice will have no authority to ship the machines to China.[9]
Along with multiple patterning, EUV has paved the way for higher transistor densities, allowing production higher-performance processors. Smaller transistors also require less power to operate, resulting in more energy-efficient electronics.
Market growth projection
[edit]According to a report by Pragma Market Research,[10] the global extreme ultraviolet (EUV) lithography market is projected to grow from US$8,957.8 million in 2024 to US$17,350 million by 2030, at a compound annual growth rate (CAGR) of 11.7%. This significant growth reflects the rising demand for miniaturized electronics in various sectors, including smartphones, artificial intelligence, and high-performance computing.
Fab tool output
[edit]Requirements for EUV steppers, given the number of layers in the design that require EUV, the number of machines, and the desired throughput of the fab, assuming 24 hours per day operation.[11]
Number of layers requiring EUV |
Avg. stepper speed in wafers per hour |
Number of EUV machines |
Wafer per month |
---|---|---|---|
5 | 62.5 | 5 | 45000 |
10 | 62.5 | 10 | 45000 |
15 | 62.5 | 15 | 45000 |
15 | 62.5 | 30 | 90000 |
20 | 62.5 | 40 | 90000 |
25 | 62.5 | 50 | 90000 |
Masks
[edit]EUV photomasks work by reflecting light,[12] which is achieved by using multiple alternating layers of molybdenum and silicon. This is in contrast to conventional photomasks which work by blocking light using a single chromium layer on a quartz substrate. An EUV mask consists of 40–50[13] alternating silicon and molybdenum layers;[14] this is a multilayer which acts to reflect the extreme ultraviolet light through Bragg diffraction; the reflectance is a strong function of incident angle and wavelength, with longer wavelengths reflecting more near normal incidence and shorter wavelengths reflecting more away from normal incidence. The multilayer may be protected by a thin ruthenium layer, called a capping layer.[13][15][16] The pattern is defined in a tantalum-based absorbing layer over the capping layer.[17]
Blank photomasks are mainly made by two companies: AGC Inc. and Hoya Corporation.[18] Ion-beam deposition equipment mainly made by Veeco is often used to deposit the multilayer.[13] A blank photomask is covered with photoresist, which is then baked (solidified) in an oven, and later the pattern is defined on the photoresist using maskless lithography with an electron beam. This step is called exposure.[19] The exposed photoresist is developed (removed), and the unprotected areas are etched. The remaining photoresist is then removed. Masks are then inspected and later repaired using an electron beam.[20] Etching must be done only in the absorbing layer[13] and thus there is a need to distinguish between the capping and the absorbing layer, which is known as etch selectivity[21] and is unlike etching in conventional photomasks, which only have one layer critical to their function.[22]
Tool
[edit]![](http://up.wiki.x.io/wikipedia/commons/thumb/3/36/Extreme_ultraviolet_lithography_tool.jpg/300px-Extreme_ultraviolet_lithography_tool.jpg)
An EUV tool (EUV photolithography machine) has a laser-driven tin (Sn) plasma light source, reflective optics comprising multilayer mirrors, contained within a hydrogen gas ambient.[23] The hydrogen is used to keep the EUV collector mirror, as the first mirror collecting EUV emitted over a large range in angle (~2π sr) from the Sn plasma, in the source free of Sn deposition.[24] Specifically, the hydrogen buffer gas in the EUV source chamber or vessel decelerates or possibly pushes back Sn ions and Sn debris traveling toward the EUV collector (collector protection) and enable a chemical reaction of to remove Sn deposition on the collector in the form of gas (collector reflectivity restoration).
EUVL is a significant departure from the deep-ultraviolet lithography standard. All matter absorbs EUV radiation. Hence, EUV lithography requires vacuum. All optical elements, including the photomask, must use defect-free molybdenum/silicon (Mo/Si) multilayers (consisting of 50 Mo/Si bilayers, which theoretical reflectivity limit at 13.5 nm is ~75%[25]) that act to reflect light by means of interlayer wave interference; any one of these mirrors absorb around 30% of the incident light, so the mirror temperature control is important.
Current EUVL systems contain at least two condenser multilayer mirrors, six projection multilayer mirrors and a multilayer object (mask). Since the mirrors absorb 96% of the EUV light, the ideal EUV source needs to be much brighter than its predecessors. EUV source development has focused on plasmas generated by laser or discharge pulses. The mirror responsible for collecting the light is directly exposed to the plasma and is vulnerable to damage from high-energy ions[26][27] and other debris[28] such as tin droplets, which require the costly collector mirror to be replaced every year.[29]
Resource requirements
[edit]Utility | 200 W output EUV | 90 W output ArF immersion double-patterning |
---|---|---|
Electrical power (kW) | 532 | 49 |
Cooling water flow (L/min) | 1600 | 75 |
Gas lines | 6 | 3 |
The required utility resources are significantly larger for EUV compared to 193 nm immersion, even with two exposures using the latter. At the 2009 EUV Symposium, Hynix reported that the wall plug efficiency was ~0.02% for EUV, i.e., to get 200 watts at intermediate focus for 100 wafers per hour, one would require 1 megawatt of input power, compared to 165 kilowatts for an ArF immersion scanner, and that even at the same throughput, the footprint of the EUV scanner was ~3× the footprint of an ArF immersion scanner, resulting in productivity loss.[30] Additionally, to confine ion debris, a superconducting magnet may be required.[31]
A typical EUV tool weighs nearly 200 tons[32] and costs around 180 million USD.[33]
EUV tools consume at least 10× more energy than immersion tools.[34]
Platform Parameter
|
DUV immersion NXT:2050i |
EUV NXE:3400C (30 mJ/cm2) | |
---|---|---|---|
Energy consumption | 0.13 MW | 1.31 MW | |
Energy efficiency per wafer pass | 0.45 kWh | 9.64 kWh | |
Throughput, wafers |
per hour | 296 | 136 |
per year | 2,584,200 | 1,191,360 |
Summary of key features
[edit]The following table summarizes key differences between EUV systems in development and ArF immersion systems which are widely used in production today:
EUV | ArF immersion | |
---|---|---|
Wavelength | 2% FWHM bandwidth about 13.5 nm | 193 nm |
Photon energy | 91–93 eV | 6.4 eV |
Light source | Sn plasma produced by CO2 laser hitting Sn droplet[35][36] | ArF excimer laser |
Wavelength bandwidth | 5.9%[37] | <0.16%[38] |
Secondary electrons produced by absorption | Yes | No |
Optics | Reflective multilayers (~40% absorbing per mirror) | Transmissive lenses |
Numerical aperture (NA) | 0.25: NXE:3100 0.33: NXE:33x0 and NXE:3400B High NA (0.55): Installed in Intel in 2024 |
1.20, 1.35 |
Resolution spec k1 = resolution / (wavelength / numerical aperture) | NXE:3100: NXE:3300B: 22 nm (k1 = 0.54), 18 nm (k1 = 0.44) with off-axis illumination NXE:3350B: 16 nm (k1 = 0.39) NXE:3400B/C, NXE:3600D: 13 nm (k1 = 0.32) |
27 nm (k1 = 0.50)38 nm (k1 = 0.27) |
Flare | 4%[39] | <1%[40] |
Illumination | Central angle 6° off-axis onto reticle | On axis |
Field size | 0.25 and 0.33 NA: 26 mm × 33 mm High NA: 26 mm × 16.5 mm[41] |
26 mm × 33 mm |
Magnification | 0.25 and 0.33 NA: 4× isomorphic High NA: 4×/8× anamorphic |
4× |
Ambient | Vacuum, hydrogen | Air (exposed wafer area underwater) |
Aberration control (including thermal) | None | Yes, e.g., FlexWave[42] |
Illumination slit | Arc-shaped[43] | Rectangular[44] |
Reticle | Pattern on reflective multilayer | Pattern on transmissive substrate |
Wafer pattern shift with reticle vertical position | Yes (due to reflection); ~1:40[45] | No |
Pellicle | Available, but has issues | Yes |
Wafers per day (depends on tool and dose) | 1500 | 6000 |
Number of tools in field | >90 (all 0.33 NA tool models) | >400 |
The different degrees of resolution among the 0.33 NA tools are due to the different illumination options. Despite the potential of the optics to reach sub-20 nm resolution, secondary electrons in resist practically limit the resolution to around 20 nm (more on this below).[46]
Light source power, throughput, and uptime
[edit]![](http://up.wiki.x.io/wikipedia/commons/thumb/6/6c/NXE3400_TPT_vs_dose.png/300px-NXE3400_TPT_vs_dose.png)
Neutral atoms or condensed matter cannot emit EUV radiation. Ionization must precede EUV emission in matter. The thermal production of multicharged positive ions is only possible in a hot dense plasma, which itself strongly absorbs EUV.[47] As of 2016, the established EUV light source is a laser-pulsed tin plasma.[48] The ions absorb the EUV light they emit and are easily neutralized by electrons in the plasma to lower charge states, which produce light mainly at other, unusable wavelengths, resulting in a much reduced efficiency of light generation for lithography at higher plasma power density.
The throughput is tied to the source power, divided by the dose.[49] A higher dose requires a slower stage motion (lower throughput) if pulse power cannot be increased.
EUV collector reflectivity degrades ~0.1–0.3% per billion 50 kHz pulses (~10% in ~2 weeks), leading to loss of uptime and throughput, while even for the first few billion pulses (within one day), there is still 20% (±10%) fluctuation.[50] This could be due to the accumulating Sn residue mentioned above which is not completely cleaned off.[51][52] On the other hand, conventional immersion lithography tools for double-patterning provide consistent output for up to a year.[53]
Recently, the NXE:3400B illuminator features a smaller pupil fill ratio (PFR) down to 20% without transmission loss.[54] PFR is maximized and greater than 0.2 around a metal pitch of 45 nm.[55]
Due to the use of EUV mirrors which also absorb EUV light, only a small fraction of the source light is finally available at the wafer. There are 4 mirrors used for the illumination optics and 6 mirrors for the projection optics. The EUV mask or reticle is itself an additional mirror. With 11 reflections, only ~2% of the EUV source light is available at the wafer.[56]
The throughput is determined by the EUV resist dose, which in turn depends on the required resolution.[57] A dose of 40 mJ/cm2 is expected to be maintained for adequate throughput.[58]
Tool uptime
[edit]The EUV light source limits tool uptime besides throughput. In a two-week period, for example, over seven hours downtime may be scheduled, while total actual downtime including unscheduled issues could easily exceed a day.[56] A dose error over 2% warrants tool downtime.[56]
The wafer exposure throughput steadily expanded up to around 1000 wafers per day (per system) over the 2019–2022 period,[59][60] indicating substantial idle time, while at the same time running >120 wafers per day on a number of multipatterned EUV layers, for an EUV wafer on average.
Comparison to other lithography light sources
[edit]EUV (10–121 nm) is the band longer than X-rays (0.1–10 nm) and shorter than the hydrogen Lyman-alpha line.
While state-of-the-art 193 nm ArF excimer lasers offer intensities of 200 W/cm2,[61] lasers for producing EUV-generating plasmas need to be much more intense, on the order of 1011 W/cm2.[62] A state-of-the-art ArF immersion lithography 120 W light source requires no more than 40 kW electrical power,[63] while EUV sources are targeted to exceed 40 kW.[64]
The optical power target for EUV lithography is at least 250 W, while for other conventional lithography sources, it is much less.[56] For example, immersion lithography light sources target 90 W, dry ArF sources 45 W, and KrF sources 40 W. High-NA EUV sources are expected to require at least 500 W.[56]
EUV-specific optical issues
[edit]Reflective optics
[edit]![](http://up.wiki.x.io/wikipedia/commons/thumb/3/39/EUV_H-V_Best_Focus.png/220px-EUV_H-V_Best_Focus.png)
A fundamental aspect of EUVL tools, resulting from the use of reflective optics, is the off-axis illumination (at an angle of 6°, in different direction at different positions within the illumination slit)[65] on a multilayer mask (reticle). This leads to shadowing effects resulting in asymmetry in the diffraction pattern that degrade pattern fidelity in various ways as described below.[66][67] For example, one side (behind the shadow) would appear brighter than the other (within the shadow).[68]
The behavior of light rays within the plane of reflection (affecting horizontal lines) is different from the behavior of light rays out of the plane of reflection (affecting vertical lines).[69] Most conspicuously, identically sized horizontal and vertical lines on the EUV mask are printed at different sizes on the wafer.
![](http://up.wiki.x.io/wikipedia/commons/thumb/2/22/36_nm_pitch_2-bar_CD_delta_vs_focus.png/220px-36_nm_pitch_2-bar_CD_delta_vs_focus.png)
The combination of the off-axis asymmetry and the mask shadowing effect leads to a fundamental inability of two identical features even in close proximity to be in focus simultaneously.[70] One of EUVL's key issues is the asymmetry between the top and bottom line of a pair of horizontal lines (the so-called "two-bar"). Some ways to partly compensate are the use of assist features as well as asymmetric illumination.[71]
An extension of the two-bar case to a grating consisting of many horizontal lines shows similar sensitivity to defocus.[72] It is manifest in the critical dimension (CD) difference between the top and bottom edge lines of the set of 11 horizontal lines.
Polarization by reflection also leads to partial polarization of EUV light, which favors imaging of lines perpendicular to the plane of the reflections.[73][74]
Pattern shift from defocus (non-telecentricity)
[edit]![](http://up.wiki.x.io/wikipedia/commons/thumb/7/7c/P28_dipole_leaf_image_fading.png/300px-P28_dipole_leaf_image_fading.png)
The EUV mask absorber, due to partial transmission, generates a phase difference between the 0th and 1st diffraction orders of a line-space pattern, resulting in image shifts (at a given illumination angle) as well as changes in peak intensity (leading to linewidth changes) which are further enhanced due to defocus.[75][76] Ultimately, this results in different positions of best focus for different pitches and different illumination angles. Generally, the image shift is balanced out due to illumination source points being paired (each on opposite sides of the optical axis). However, the separate images are superposed and the resulting image contrast is degraded when the individual source image shifts are large enough. The phase difference ultimately also determines the best focus position.
The multilayer is also responsible for image shifting due to phase shifts from diffracted light within the multilayer itself.[77] This is inevitable due to light passing twice through the mask pattern.[78]
The use of reflection causes wafer exposure position to be extremely sensitive to the reticle flatness and the reticle clamp. Reticle clamp cleanliness is therefore required to be maintained. Small (milliradian-scale) deviations in mask flatness in the local slope, coupled with wafer defocus.[79] More significantly, mask defocus has been found to result in large overlay errors.[80][81] In particular, for a 10 nm node metal 1 layer (including 48 nm, 64 nm, 70 nm pitches, isolated, and power lines), the uncorrectable pattern placement error was 1 nm for 40 nm mask z-position shift.[82] This is a global pattern shift of the layer with respect to previously defined layers. However, features at different locations will also shift differently due to different local deviations from mask flatness, e.g., from defects buried under the multilayer. It can be estimated that the contribution of mask non-flatness to overlay error is roughly 1/40 times the peak-to-valley thickness variation.[83] With the blank peak-to-valley spec of 50 nm, ~1.25 nm image placement error is possible. Blank thickness variations up to 80 nm also contribute, which lead to up to 2 nm image shift.[83]
The off-axis illumination of the reticle is also the cause of non-telecentricity in wafer defocus, which consumes most of the 1.4 nm overlay budget of the NXE:3400 EUV scanner[84] even for design rules as loose as 100 nm pitch.[85] The worst uncorrectable pattern placement error for a 24 nm line was about 1.1 nm, relative to an adjacent 72 nm power line, per 80 nm wafer focus position shift at a single slit position; when across-slit performance is included, the worst error is over 1.5 nm in the wafer defocus window[82] In 2017, an actinic microscope mimicking a 0.33 NA EUV lithography system with 0.2/0.9 quasar 45 illumination showed that an 80 nm pitch contact array shifted −0.6 to 1.0 nm while a 56 nm pitch contact array shifted −1.7 to 1.0 nm relative to a horizontal reference line, within a ±50 nm defocus window.[86]
Wafer defocus also leads to image placement errors due to deviations from local mask flatness. If the local slope is indicated by an angle α, the image is projected to be shifted in a 4× projection tool by 8α × (DOF/2) = 4α DOF, where DOF is the depth of focus.[87] For a depth of focus of 100 nm, a small local deviation from flatness of 2.5 mrad (0.14°) can lead to a pattern shift of 1 nm.
Simulations as well as experiments have shown that pupil imbalances in EUV lithography can result in pitch-dependent pattern placement errors.[88][89] Since the pupil imbalance changes with EUV collector mirror aging or contamination, such placement errors may not be stable over time. The situation is specifically challenging for logic devices, where multiple pitches have critical requirements at the same time.[90] The issue is ideally addressed by multiple exposures with tailored illuminations.[91]
Slit position dependence
[edit]![](http://up.wiki.x.io/wikipedia/commons/thumb/a/a6/Rotated_EUV_illumination_through_slit.png/350px-Rotated_EUV_illumination_through_slit.png)
The direction of illumination is also highly dependent on slit position, essentially rotated azimuthally.[95][96][43][97][98][99] Nanya Technology and Synopsys found that horizontal vs. vertical bias changed across slit with dipole illumination.[100] The rotating plane of incidence (azimuthal range within −25° to 25°) is confirmed in the SHARP actinic review microscope at CXRO which mimics the optics for EUV projection lithography systems.[101] The reason for this is a mirror is used to transform straight rectangular fields into arc-shaped fields.[102][103] In order to preserve a fixed plane of incidence, the reflection from the previous mirror would be from a different angle with the surface for a different slit position; this causes non-uniformity of reflectivity. To preserve uniformity, rotational symmetry with a rotating plane of incidence is used.[104] More generally, so-called "ring-field" systems reduce aberrations by relying on the rotational symmetry of an arc-shaped field derived from an off-axis annulus.[105] This is preferred, as reflective systems must use off-axis paths, which aggravate aberrations. Hence identical die patterns within different halves of the arc-shaped slit would require different OPC. This renders them uninspectable by die-to-die comparison, as they are no longer truly identical dies. For pitches requiring dipole, quadrupole, or hexapole illumination, the rotation also causes mismatch with the same pattern layout at a different slit position, i.e., edge vs. center. Even with annular or circular illumination, the rotational symmetry is destroyed by the angle-dependent multilayer reflectance described above. Although the azimuthal angle range is about ±20°[106] (NXE3400[107] field data indicate 18.2°[108]) on 0.33 NA scanners, at 7 nm design rules (36–40 nm pitch), the tolerance for illumination can be ±15°,[109][110] or even less.[111][112][107] Annular illumination nonuniformity and asymmetry also significantly impact the imaging.[113] At 28 nm pitch, the required dipole illumination becomes impossible to maintain across slit on 0.33 NA EUV systems.[114]
The larger incident angle for pitch-dependent dipole illumination trend across slit does not affect horizontal line shadowing so much, but vertical line shadowing does increase going from center to edge.[115] In addition, higher-NA systems may offer limited relief from shadowing, as they target tighet pitches.[115]
![](http://up.wiki.x.io/wikipedia/commons/thumb/2/2e/H_and_V_shadowing_across_EUV_slit.png/300px-H_and_V_shadowing_across_EUV_slit.png)
The slit position dependence is particularly difficult for the tilted patterns encountered in DRAM.[98] Besides the more complicated effects due to shadowing and pupil rotation, tilted edges are converted to stair shape, which may be distorted by OPC. In fact, the 32 nm pitch DRAM by EUV will lengthen up to at least 9F2 cell area, where F is the active area half-pitch (traditionally, it had been 6F2).[100] With a 2-D self-aligned double-patterning active area cut, the cell area is still lower at 8.9F2.[116]
Aberrations, originating from deviations of optical surfaces from subatomic (<0.1 nm) specifications[117] as well as thermal deformations[118][119] and possibly including polarized reflectance effects,[120] are also dependent on slit position,[121][119] as will be further discussed below, with regard to source-mask optimization (SMO). The thermally induced aberrations are expected to exhibit differences among different positions across the slit, corresponding to different field positions, as each position encounters different parts of the deformed mirrors.[122] Ironically, the use of substrate materials with high thermal and mechanical stability make it more difficult to compensate wavefront errors[123]
In combination with the range of wavelengths, the rotated plane of incidence aggravates the already severe stochastic impact on EUV imaging.[124]
Wavelength bandwidth (chromatic aberration)
[edit]![](http://up.wiki.x.io/wikipedia/commons/thumb/d/d2/Defocus_pattern_shift_vs_wavelength.png/300px-Defocus_pattern_shift_vs_wavelength.png)
Unlike deep ultraviolet (DUV) lithography sources, based on excimer lasers, EUV plasma sources produce light across a broad range of wavelengths[125] roughly spanning a 2% FWHM bandwidth near 13.5 nm (13.36nm – 13.65nm at 50% power). EUV (10–121nm) is the band longer than X-Rays (0.1–10nm) and shorter than the hydrogen Lyman-alpha line.
Though the EUV spectrum is not completely monochromatic, nor even as spectrally pure as DUV laser sources, the working wavelength has generally been taken to be 13.5 nm. In actuality, the reflected power is distributed mostly in the 13.3-13.7 nm range.[126] The bandwidth of EUV light reflected by a multilayer mirror used for EUV lithography is over +/-2% (>270 pm);[127] the phase changes due to wavelength changes at a given illumination angle may be calculated[128] and compared to the aberration budget.[129] Wavelength dependence of reflectance[128][126] also affects the apodization, or illumination distribution across the pupil (for different angles); different wavelengths effectively 'see' different illuminations as they are reflected differently by the multilayer of the mask.[130][126] This effective source illumination tilt can lead to large image shifts due to defocus.[131] Conversely, the peak reflected wavelength varies across the pupil due to different incident angles.[126][132] This is aggravated when the angles span a wide radius, e.g., annular illumination. The peak reflectance wavelength increases for smaller incident angles.[133] Aperiodic multilayers have been proposed to reduce the sensitivity at the cost of lower reflectivity but are too sensitive to random fluctuations of layer thicknesses, such as from thickness control imprecision or interdiffusion.[134]
A narrower bandwidth would increase sensitivity to mask absorber and buffer thickness on the 1 nm scale.[135]
Flare
[edit]Flare is the presence of background light originating from scattering off of surface features which are not resolved by the light. In EUV systems, this light can be EUV or out-of-band (OoB) light that is also produced by the EUV source. The OoB light adds the complication of affecting the resist exposure in ways other than accounted for by the EUV exposure. OoB light exposure may be alleviated by a layer coated above the resist, as well as 'black border' features on the EUV mask.[136] However, the layer coating inevitably absorbs EUV light, and the black border adds EUV mask processing cost.
Line tip effects
[edit]A key challenge for EUV is the counter-scaling behavior of the line tip-to-tip (T2T) distance as half-pitch (hp) is scaled down.[111] This is in part due to lower image contrast for the binary masks used in EUV lithography, which is not encountered with the use of phase shift masks in immersion lithography.[137][138] The rounding of the corners of the line end leads to line end shortening,[139] and this is worse for binary masks.[140] The use of phase-shift masks in EUV lithography has been studied but encounters difficulties from phase control in thin layers[141] as well as the bandwidth of the EUV light itself.[142] More conventionally, optical proximity correction (OPC) is used to address the corner rounding and line-end shortening. In spite of this, it has been shown that the tip-to-tip resolution and the line tip printability are traded off against each other, being effectively CDs of opposite polarity.[143]
In unidirectional metal layers, tip-to-tip spacing is one of the more severe issues for single exposure patterning. For the 40 nm pitch vertical lines, an 18 nm nominal tip-to-tip drawn gap resulted in an actual tip-to-tip distance of 29 nm with OPC,[111] while for 32 nm pitch horizontal lines, the tip-to-tip distance with a 14 nm nominal gap went to 31 nm with OPC.[144] These actual tip-to-tip distances define a lower limit of the half-pitch of the metal running in the direction perpendicular to the tip. In this case, the lower limit is around 30 nm. With further optimization of the illumination (discussed in the section on source-mask optimization), the lower limit can be further reduced to around 25 nm.[145]
For larger pitches, where conventional illumination can be used, the line tip-to-tip distance is generally larger. For the 24 nm half-pitch lines, with a 20 nm nominally drawn gap, the distance was actually 45 nm, while for 32 nm half-pitch lines, the same nominal gap resulted in a tip-to-tip distance of 34 nm.[144] With OPC, these become 39 nm and 28 nm for 24 nm half-pitch and 32 nm half-pitch, respectively.[146]
Enhancement opportunities for EUV patterning
[edit]Assist features
[edit]![](http://up.wiki.x.io/wikipedia/commons/thumb/1/1d/Assist_feature_OPC.png/300px-Assist_feature_OPC.png)
Assist features are often used to help balance asymmetry from non-telecentricity at different slit positions, due to different illumination angles, starting at the 7 nm node,[147][148] where the pitch is ~ 41 nm for a wavelength ~13.5 nm and NA=0.33, corresponding to k1 ~ 0.5.[149] However, the asymmetry is reduced but not eliminated, since the assist features mainly enhance the highest spatial frequencies, whereas intermediate spatial frequencies, which also affect feature focus and position, are not much affected. The coupling between the primary image and the self images is too strong for the asymmetry to be eliminated by assist features; only asymmetric illumination can achieve this.[71] Assist features may also get in the way of access to power/ground rails. Power rails are expected to be wider, which also limits the effectiveness of using assist features, by constraining the local pitch. Local pitches between 1× and 2× the minimum pitch forbid assist feature placement, as there is simply no room to preserve the local pitch symmetry. In fact, for the application to the two-bar asymmetry case, the optimum assist feature placement may be less than or exceed the two-bar pitch.[148] Depending on the parameter to be optimized (process window area, depth of focus, exposure latitude), the optimum assist feature configuration can be very different, e.g., pitch between assist feature and bar being different from two-bar pitch, symmetric or asymmetric, etc..
At pitches smaller than 58 nm, there is a tradeoff between depth of focus enhancement and contrast loss by assist feature placement.[148] Generally, there is still a focus-exposure tradeoff as the dose window is constrained by the need to have the assist features not print accidentally.
An additional concern comes from shot noise;[150] sub-resolution assist features (SRAFs) cause the required dose to be lower, so as not to print the assist features accidentally.[151] This results in fewer photons defining smaller features (see discussion in section on shot noise).
As SRAFs are smaller features than primary features and are not supposed to receive doses high enough to print, they are more susceptible to stochastic dose variations causing printing errors; this is particularly prohibitive for EUV, where phase-shift masks may need to be used.[152]
Source-mask optimization
[edit]![](http://up.wiki.x.io/wikipedia/commons/thumb/b/b6/EUV_SMO_effectiveness_vs._pitch.png/250px-EUV_SMO_effectiveness_vs._pitch.png)
Due to the effects of non-telecentricity, standard illumination pupil shapes, such as disc or annular, are not sufficient to be used for feature sizes of ~20 nm or below (10 nm node and beyond).[85] Instead certain parts of the pupil (often over 50%) must be asymmetrically excluded. The parts to be excluded depend on the pattern. In particular, the densest allowed lines need to be aligned along one direction and prefer a dipole shape. For this situation, double exposure lithography would be required for 2D patterns, due to the presence of both X- and Y-oriented patterns, each requiring its own 1D pattern mask and dipole orientation.[153][154] There may be 200–400 illuminating points, each contributing its weight of the dose to balance the overall image through focus. Thus the shot noise effect (to be discussed later) critically affects the image position through focus, in a large population of features.
Double- or multiple-patterning would also be required if a pattern consists of sub-patterns which require significantly different optimized illuminations, due to different pitches, orientations, shapes, and sizes.
Impact of slit position and aberrations
[edit]![](http://up.wiki.x.io/wikipedia/commons/thumb/3/38/EUV_pupil_wavelength_dependence.png/300px-EUV_pupil_wavelength_dependence.png)
Largely due to the slit shape,[106] and the presence of residual aberrations,[155] the effectiveness of SMO varies across slit position.[156] At each slit position, there are different aberrations[121] and different azimuthal angles of incidence leading to different shadowing.[43] Consequently, there could be uncorrected variations across slit for aberration-sensitive features, which may not be obviously seen with regular line-space patterns.[148] At each slit position, although optical proximity correction (OPC), including the assist features mentioned above, may also be applied to address the aberrations,[157][158] they also feedback into the illumination specification,[159][156][160][161] since the benefits differ for different illumination conditions.[157] This would necessitate the use of different source-mask combinations at each slit position, i.e., multiple mask exposures per layer.[121][162]
The above-mentioned chromatic aberrations, due to mask-induced apodization,[130] also lead to inconsistent source-mask optimizations for different wavelengths.
Pitch-dependent focus windows
[edit]The best focus for a given feature size varies as a strong function of pitch, polarity, and orientation under a given illumination.[163] At 36 nm pitch, horizontal and vertical darkfield features have more than 30 nm difference of focus. The 34 nm pitch and 48 nm pitch features have the largest difference of best focus regardless of feature type. In the 48–64 nm pitch range, the best focus position shifts roughly linearly as a function of pitch, by as much as 10–20 nm.[164] For the 34–48 nm pitch range, the best focus position shifts roughly linearly in the opposite direction as a function of pitch. This can be correlated with the phase difference between the zero and first diffraction orders.[165] Assist features, if they can fit within the pitch, were found not to reduce this tendency much, for a range of intermediate pitches,[166] or even worsened it for the case of 18–27 nm and quasar illumination.[167] 50 nm contact holes on 100 nm and 150 pitches had best focus positions separated by roughly 25 nm; smaller features are expected to be worse.[168] Contact holes in the 48–100 nm pitch range showed a 37 nm best focus range.[169] The best focus position vs. pitch is also dependent on resist.[170] Critical layers often contain lines at one minimum pitch of one polarity, e.g., darkfield trenches, in one orientation, e.g., vertical, mixed with spaces of the other polarity of the other orientation. This often magnifies the best focus differences, and challenges the tip-to-tip and tip-to-line imaging.[171]
Reduction of pupil fill
[edit]![](http://up.wiki.x.io/wikipedia/commons/thumb/4/48/Screenshot_20230216_130758_PowerPoint.jpg/300px-Screenshot_20230216_130758_PowerPoint.jpg)
A consequence of SMO and shifting focus windows has been the reduction of pupil fill. In other words, the optimum illumination is necessarily an optimized overlap of the preferred illuminations for the various patterns that need to be considered. This leads to lower pupil fill providing better results. However, throughput is affected below 20% pupil fill due to absorption.[172][173][54]
Phase shift masks
[edit]![](http://up.wiki.x.io/wikipedia/commons/thumb/9/97/EUV_attPSM_near_field_phase.png/250px-EUV_attPSM_near_field_phase.png)
A commonly touted advantage of EUV has been the relative ease of lithography, as indicated by the ratio of feature size to the wavelength multiplied by the numerical aperture, also known as the k1 ratio. An 18 nm metal linewidth has a k1 of 0.44 for 13.5 nm wavelength, 0.33 NA, for example. For the k1 approaching 0.5, some weak resolution enhancement including attenuated phase shift masks has been used as essential to production with the ArF laser wavelength (193 nm),[174][175][176][177][178][179] whereas this resolution enhancement is not available for EUV.[180][181][182] In particular, 3D mask effects including scattering at the absorber edges distort the desired phase profile.[181] Also, the phase profile is effectively derived from the plane wave spectrum reflected from the multilayer through the absorber rather than the incident plane wave.[183] Without absorbers, near-field distortion also occurs at an etched multilayer sidewall due to the oblique incidence illumination;[184] some light traverses only a limited number of bilayers near the sidewall.[68] Additionally, the different polarizations (TE and TM) have different phase shifts.[68].Fundamentally, a chromeless phase shift mask enables pitch splitting by suppression of the zeroth diffracted order on the mask, but fabricating a high quality phase shift mask for EUV is certainly not a trivial task. One possible way to achieve this is through spatial filtering at the Fourier plane of the mask pattern. At Lawrence Berkeley National Lab, the light of the zeroth order is a centrally obscured system, and the +/-1 diffracted orders will be captured by the clear aperture, providing a functional equivalent to the chromeless phase shift mask while using a conventional binary amplitude mask.[185]
EUV photoresist exposure: the role of electrons
[edit]EUV light generates photoelectrons upon absorption by matter. These photoelectrons in turn generate secondary electrons, which slow down before engaging in chemical reactions.[186] At sufficient doses 40 eV electrons are known to penetrate 180 nm thick resist leading to development.[187] At a dose of 160 μC/cm2, corresponding to 15 mJ/cm2 EUV dose assuming one electron/photon, 30 eV electrons removed 7 nm of PMMA resist after standard development.[188] For a higher 30 eV dose of 380 μC/cm2, equivalent to 36 mJ/cm2 at one electron/photon, 10.4 nm of PMMA resist are removed.[189] These indicate the distances the electrons can travel in resist, regardless of direction.[190]
The degree of photoelectron emission from the layer underlying the EUV photoresist has been shown to affect the depth of focus.[191] Unfortunately, hardmask layers tend to increase photoelectron emission, degrading the depth of focus. Electrons from defocused images in the resist can also affect the best focus image.[192]
The randomness of the number of secondary electrons is itself a source of stochastic behavior in EUV resist images. The scale length of electron blur itself has a distribution.[193] Intel demonstrated with a rigorous simulation that EUV-released electrons scatter distances larger than 15 nm in EUV resists.[194]
The electron blur is also affected by total internal reflection from the top surface of the resist film.[195][196]
Effect of underlying layers
[edit]![](http://up.wiki.x.io/wikipedia/commons/thumb/5/51/Secondary_Electrons_from_Layers_under_EUV_Resist.png/300px-Secondary_Electrons_from_Layers_under_EUV_Resist.png)
Secondary electrons from layers underneath the resist can affect the resist profile as well as pattern collapse.[197] Hence, selection of such both the underlayer and the layer under that layer are important considerations for EUV lithography. Moreover, the electrons from defocused images can aggravate the stochastic nature of the image.[198]
Contamination effects
[edit]Resist outgassing
[edit]![](http://up.wiki.x.io/wikipedia/commons/thumb/e/e0/Outgassing_contamination_vs_dose.png/300px-Outgassing_contamination_vs_dose.png)
Due to the high efficiency of absorption of EUV by photoresists, heating and outgassing become primary concerns. One well-known issue is contamination deposition on the resist from ambient or outgassed hydrocarbons, which results from EUV- or electron-driven reactions.[199] Organic photoresists outgas hydrocarbons[200] while metal oxide photoresists outgas water and oxygen[201] and metal (in a hydrogen ambient); the last is uncleanable.[52] The carbon contamination is known to affect multilayer reflectivity[202] while the oxygen is particularly harmful for the ruthenium capping layers (relatively stable under EUV and hydrogen conditions) on the EUV multilayer optics.[203]
Tin redeposition
[edit]Atomic hydrogen in the tool chambers is used to clean tin and carbon which deposit on the EUV optical surfaces.[204] Atomic hydrogen is produced by EUV light directly photoionizing H2:[205]
- hν + H2 → H+ + H + e−.
Electrons generated in the above reaction may also dissociate H2 to form atomic hydrogen:[205]
- e− + H2 → H+ + H + 2e−.
The reaction with tin in the light source (e.g., tin on an optical surface in the source) to form volatile SnH4 (stannane) that can be pumped out from the source proceeds via the reaction[204]
- Sn(s) + 4 H(g) → SnH4(g).
The SnH4 can reach the coatings of other EUV optical surfaces, where it redeposits Sn via the reaction[204]
- SnH4 → Sn(s) + 2 H2(g).
Redeposition may also occur by other intermediate reactions.[206]
The redeposited Sn[51][52] might be subsequently removed by atomic-hydrogen exposure. However, overall, the tin cleaning efficiency (the ratio of the removed tin flux from a tin sample to the atomic-hydrogen flux to the tin sample) is less than 0.01%, due to both redeposition and hydrogen desorption, leading to formation of hydrogen molecules at the expense of atomic hydrogen.[204] The tin cleaning efficiency for tin oxide is found roughly twice higher than that of tin (with a native oxide layer of ~2 nm on it).[204] Injecting a small amount of oxygen to the light source may improve the tin cleaning rate.
Hydrogen blistering
[edit]![](http://up.wiki.x.io/wikipedia/commons/thumb/f/f3/Atomic_hydrogen_in_multilayer.png/300px-Atomic_hydrogen_in_multilayer.png)
Hydrogen also reacts with metal-containing compounds to reduce them to metal,[207] and diffuses through the silicon[208] and molybdenum[209] in the multilayer, eventually causing blistering.[210][211][212] Capping layers that mitigate hydrogen-related damage often reduce reflectivity to well below 70%.[211] Capping layers are known to be permeable to ambient gases including oxygen[213] and hydrogen,[214][215][216][217] as well as susceptible to the hydrogen-induced blistering defects.[218][210] Hydrogen may also react with the capping layer, resulting in its removal.[219]
Tin spitting
[edit]Hydrogen can penetrate molten tin (Sn), creating hydrogen bubbles inside it. If the bubbles move at the molten tin surface, then it bursts with tin, resulting in tin spreading over a large angle range. This phenomenon is called tin spitting and is one of EUV Collector contamination sources.
Resist erosion
[edit]Hydrogen also reacts with resists to etch[220][221] or decompose[222] them. Besides photoresist, hydrogen plasmas can also etch silicon, albeit very slowly.[223][non-primary source needed]
Membrane
[edit]To help mitigate the above effects, the latest EUV tool introduced in 2017, the NXE:3400B, features a membrane that separates the wafer from the projection optics of the tool, protecting the latter from outgassing from the resist on the wafer.[54] The membrane contains layers which absorb DUV and IR radiation, and transmits 85–90% of the incident EUV radiation. There is of course, accumulated contamination from wafer outgassing as well as particles in general (although the latter are out of focus, they may still obstruct light).
EUV-induced plasma
[edit]![](http://up.wiki.x.io/wikipedia/commons/thumb/9/96/Spread_of_electrons_outside_EUV_exposure_area.png/220px-Spread_of_electrons_outside_EUV_exposure_area.png)
EUV lithographic systems using EUV light operate in 1–10 Pa hydrogen background gas.[224] The plasma is a source of VUV radiation[225] as well as electrons and hydrogen ions[226] This plasma is known to etch exposed materials.[226][227]
In 2023, a study supported at TSMC was published which indicated net charging by electrons from the plasma as well as from electron emission.[228] The charging was found to occur even outside the EUV exposure area, indicating that the surrounding area had been exposed to electrons.
Due to chemical sputtering of carbon by the hydrogen plasma,[229] there can be generation of nanoparticles,[230] which can obstruct the EUV resist exposure.[231][232]
Mask defects
[edit]![](http://up.wiki.x.io/wikipedia/commons/thumb/1/1d/EUVL_printable_defects.png/300px-EUVL_printable_defects.png)
Reducing defects on extreme ultraviolet (EUV) masks is currently one of the most critical issues to be addressed for commercialization of EUV lithography.[233] Defects can be buried underneath or within the multilayer stack[234] or be on top of the multilayer stack. Mesas or protrusions form on the sputtering targets used for multilayer deposition, which may fall off as particles during the multilayer deposition.[235] In fact, defects of atomic scale height (0.3–0.5 nm) with 100 nm FWHM can still be printable by exhibiting 10% CD impact.[236] IBM and Toppan reported at Photomask Japan 2015 that smaller defects, e.g., 50 nm size, can have 10% CD impact even with 0.6 nm height, yet remain undetectable.[237]
Furthermore, the edge of a phase defect will further reduce reflectivity by more than 10% if its deviation from flatness exceeds 3 degrees, due to the deviation from the target angle of incidence of 84 degrees with respect to the surface. Even if the defect height is shallow, the edge still deforms the overlying multilayer, producing an extended region where the multilayer is sloped. The more abrupt the deformation, the narrower the defect edge extension, the greater the loss in reflectivity.
EUV mask defect repair is also more complicated due to the across-slit illumination variation mentioned above. Due to the varying shadowing sensitivity across the slit, the repair deposition height must be controlled very carefully, being different at different positions across the EUV mask illumination slit.[238]
Multilayer reflectivity random variations
[edit]GlobalFoundries and Lawrence Berkeley Labs carried out a Monte Carlo study to simulate the effects of intermixing between the molybdenum (Mo) and silicon (Si) layers in the multilayer that is used to reflect EUV light from the EUV mask.[239] The results indicated high sensitivity to the atomic-scale variations of layer thickness. Such variations could not be detected by wide-area reflectivity measurements but would be significant on the scale of the critical dimension (CD).[239] The local variation of reflectivity could be on the order of 10% for a few nm standard deviation.[240]
Multilayer damage
[edit]Multiple EUV pulses at less than 10 mJ/cm2 could accumulate damage to a Ru-capped Mo/Si multilayer mirror optic element.[241] The angle of incidence was 16° or 0.28 rads, which is within the range of angles for a 0.33 NA optical system.
Pellicles
[edit]Production EUV tools need a pellicle to protect the mask from contamination. Pellicles are normally expected to protect the mask from particles during transport, entry into or exit from the exposure chamber, as well as the exposure itself. Without pellicles, particle adders would reduce yield, which has not been an issue for conventional optical lithography with 193 nm light and pellicles. However, for EUV, the feasibility of pellicle use is severely challenged, due to the required thinness of the shielding films to prevent excessive EUV absorption. Particle contamination would be prohibitive if pellicles were not stable above 200 W, i.e., the targeted power for manufacturing.[242]
Heating of the EUV mask pellicle (film temperature up to 750 K for 80 W incident power) is a significant concern, due to the resulting deformation and transmission decrease.[243] ASML developed a 70 nm thick polysilicon pellicle membrane, which allows EUV transmission of 82%; however, less than half of the membranes survived expected EUV power levels.[244] SiNx pellicle membranes also failed at 82 W equivalent EUV source power levels.[245] At target 250 W levels, the pellicle is expected to reach 686 degrees Celsius,[246] well over the melting point of aluminum. Alternative materials need to allow sufficient transmission as well as maintain mechanical and thermal stability. However, graphite, graphene or other carbon nanomaterials (nanosheets, nanotubes) are damaged by EUV due to the release of electrons[247] and also too easily etched in the hydrogen cleaning plasma expected to be deployed in EUV scanners.[248] Hydrogen plasmas can also etch silicon as well.[249][250] A coating helps improve hydrogen resistance, but this reduces transmission and/or emissivity, and may also affect mechanical stability (e.g., bulging).[251]
Wrinkles on pellicles can cause CD nonuniformity due to uneven absorption; this is worse for smaller wrinkles and more coherent illumination, i.e., lower pupil fill.[252]
In the absence of pellicles, EUV mask cleanliness would have to be checked before actual product wafers are exposed, using wafers specially prepared for defect inspection.[253] These wafers are inspected after printing for repeating defects indicating a dirty mask; if any are found, the mask must be cleaned and another set of inspection wafers are exposed, repeating the flow until the mask is clean. Any affected product wafers must be reworked.
TSMC reported starting limited use of its own pellicle in 2019 and continuing to expand afterwards,[254] and Samsung is planning pellicle introduction in 2022.[255]
Hydrogen bulging defects
[edit]As discussed above, with regard to contamination removal, hydrogen used in recent EUV systems can penetrate into the EUV mask layers. TSMC indicated in its patent that hydrogen would enter from the mask edge.[256] Once trapped, bulge defects or blisters were produced,[218] which could lead to film peeling.[256] These are essentially the blister defects which arise after a sufficient number of EUV mask exposures in the hydrogen environment.
EUV stochastic issues
[edit]![](http://up.wiki.x.io/wikipedia/commons/1/1f/64_nm_pitch_EUV_shot_noise.png)
EUV lithography is particularly sensitive to stochastic effects.[257][258] In a large population of features printed by EUV, although the overwhelming majority are resolved, some suffer complete failure to print, e.g. missing holes or bridging lines. A known significant contribution to this effect is the dose used to print.[259] This is related to shot noise, to be discussed further below. Due to the stochastic variations in arriving photon numbers, some areas designated to print actually fail to reach the threshold to print, leaving unexposed defect regions. Some areas may be overexposed, leading to excessive resist loss or crosslinking. The probability of stochastic failure increases exponentially as feature size decreases, and for the same feature size, increasing distance between features also significantly increases the probability.[259] Line cuts which are misshapen are a significant issue due to potential arcing and shorting.[260] Yield requires detection of stochastic failures down to below 1e-12.[259]
The tendency to stochastic defects is worse from defocus over a large pupil fill.[261][262]
![](http://up.wiki.x.io/wikipedia/commons/thumb/d/d3/EUV_Stochastic_Hot_Spots.png/150px-EUV_Stochastic_Hot_Spots.png)
Multiple failure modes may exist for the same population. For example, besides bridging of trenches, the lines separating the trenches may be broken.[259] This can be attributed to stochastic resist loss,[257] from secondary electrons.[263][264] The randomness of the number of secondary electrons is itself a source of stochastic behavior in EUV resist images.
The coexistence of stochastically underexposed and overexposed defect regions leads to a loss of dose window at a certain post-etch defect level between the low-dose and high-dose patterning cliffs.[265] Hence, the resolution benefit from shorter wavelength is lost.
The resist underlayer also plays an important role.[259] This could be due to the secondary electrons generated by the underlayer.[266] Secondary electrons may remove over 10 nm of resist from the exposed edge.[263][267]
The defect level is on the order of 1K/mm2.[268] In 2020, Samsung reported that 5 nm layouts had risks for process defects and had started implementing automated check and fixing.[269]
Photon shot noise also leads to stochastic edge placement error.[270] The photon shot noise is augmented to some degree by blurring factors such as secondary electrons or acids in chemically amplified resists; when significant the blur also reduces the image contrast at the edge. An edge placement error (EPE) as large as 8.8 nm was measured for a 48 nm pitch EUV-printed metal pattern.[271]
![](http://up.wiki.x.io/wikipedia/commons/thumb/2/2a/Line_end_stochastic.png/300px-Line_end_stochastic.png)
With the natural Poisson distribution due to the random arrival and absorption times of the photons,[272][273] there is an expected natural dose (photon number) variation of at least several percent 3 sigma, making the exposure process susceptible to stochastic variations. The dose variation leads to a variation of the feature edge position, effectively becoming a blur component. Unlike the hard resolution limit imposed by diffraction, shot noise imposes a softer limit, with the main guideline being the ITRS line width roughness (LWR) spec of 8% (3s) of linewidth.[274] Increasing the dose will reduce the shot noise,[275] but this also requires higher source power.
The two issues of shot noise and EUV-released electrons point out two constraining factors: 1) keeping dose high enough to reduce shot noise to tolerable levels, but also 2) avoiding too high a dose due to the increased contribution of EUV-released photoelectrons and secondary electrons to the resist exposure process, increasing the edge blur and thereby limiting the resolution. Aside from the resolution impact, higher dose also increases outgassing[276] and limits throughput, and crosslinking[277] occurs at very high dose levels. For chemically amplified resists, higher dose exposure also increases line edge roughness due to acid generator decomposition.[278]
Even with higher absorption at the same dose, EUV has a larger shot noise concern than the ArF (193 nm) wavelength, mainly because it is applied to thinner resists.[279]
Due to stochastic considerations, the IRDS 2022 lithography roadmap now acknowledges increasing doses for smaller feature sizes.[280]
EUV resolution will likely be compromised by stochastic effects. Stochastic defect densities have exceeded 1/cm2, at 36 nm pitch.[281][282] In 2024, an EUV resist exposure by ASML revealed a missing+bridging 32 nm pitch contact hole defect density floor >0.25/cm2 (177 defects per wafer), made worse with thinner resist.[283] ASML indicated 30 nm pitch would not use direct exposure but double patterning.[284] Intel did not use EUV for 30 nm pitch.[285]
Pupil fill ratio
[edit]For pitches less than half-wavelength divided by numerical aperture, dipole illumination is necessary. This illumination fills at most a leaf-shaped area at the edge of the pupil. However, due to 3D effects in the EUV mask,[286] smaller pitches require even smaller portions of this leaf shape. Below 20% of the pupil, the throughput and dose stability begin to suffer.[54] Higher numerical aperture allows a higher pupil fill to be used for the same pitch, but depth of focus is significantly reduced.[287]
Use with multiple-patterning
[edit]EUV is anticipated to use double-patterning at around 34 nm pitch with 0.33 NA.[288][289] This resolution is equivalent to '1Y' for DRAM.[290][291] In 2020, ASML reported that 5 nm M0 layer (30 nm minimum pitch) required double-patterning.[284] In H2 2018, TSMC confirmed that its 5 nm EUV scheme still used multi-patterning,[292] also indicating that mask count did not decrease from its 7 nm node, which used extensive DUV multi-patterning, to its 5 nm node, which used extensive EUV.[293] EDA vendors also indicated the continued use of multi-patterning flows.[294][295] While Samsung introduced its own 7 nm process with EUV single-patterning,[296] it encountered severe photon shot noise causing excessive line roughness, which required higher dose, resulting in lower throughput.[272] TSMC's 5 nm node uses even tighter design rules.[297] Samsung indicated smaller dimensions would have more severe shot noise.[272]
![](http://up.wiki.x.io/wikipedia/commons/thumb/b/b9/Via_Triple_Patterning_for_EUV.png/100px-Via_Triple_Patterning_for_EUV.png)
In Intel's complementary lithography scheme at 20 nm half-pitch, EUV would be used only in a second line-cutting exposure after a first 193 nm line-printing exposure.[298]
Multiple exposures would also be expected where two or more patterns in the same layer, e.g., different pitches or widths, must use different optimized source pupil shapes.[299][300][301][302] For example, when considering a staggered bar array of 64 nm vertical pitch, changing the horizontal pitch from 64 nm to 90 nm changes the optimized illumination significantly.[55] Source-mask optimization that is based on line-space gratings and tip-to-tip gratings only does not entail improvements for all parts of a logic pattern, e.g., a dense trench with a gap on one side.[299][303]
In 2020, ASML reported that for the 3 nm node, center-to-center contact/via spacings of 40 nm or less would require double- or triple-patterning for some contact/via arrangements.[304]
For the 24–36 nm metal pitch, it was found that using EUV as a (second) cutting exposure had a significantly wider process window than as a complete single exposure for the metal layer.[305][299]
Multiple exposures of the same mask are also expected for defect management without pellicles, limiting productivity similarly to multiple-patterning.[253]
Self-aligned litho-etch-litho-etch (SALELE) is a hybrid SADP/LELE technique whose implementation has started in 7 nm.[306] Self-aligned litho-etch-litho-etch (SALELE) has become an accepted form of double-patterning to be used with EUV.[307]
Single-patterning extension: anamorphic high-NA
[edit]![](http://up.wiki.x.io/wikipedia/commons/thumb/d/d3/EUV_High-NA_stochastic_sidelobes.png/300px-EUV_High-NA_stochastic_sidelobes.png)
A return to extended generations of single-patterning would be possible with higher numerical aperture (NA) tools. An NA of 0.45 could require retuning of a few percent.[308] Increasing demagnification could avoid this retuning, but the reduced field size severely affects large patterns (one die per 26 mm × 33 mm field) such as the many-core multi-billion transistor 14 nm Xeon chips.[309] by requiring field stitching of two mask exposures.
In 2015, ASML disclosed details of its anamorphic next-generation EUV scanner, with an NA of 0.55. These machines cost around USD 360 million.[33] The demagnification is increased from 4× to 8× only in one direction (in the plane of incidence).[310] However, the 0.55 NA has a much smaller depth of focus than immersion lithography.[311] Also, an anamorphic 0.52 NA tool has been found to exhibit too much CD and placement variability for 5 nm node single exposure and multi-patterning cutting.[312]
Depth of focus[313] being reduced by increasing NA is also a concern,[314] especially in comparison with multi-patterning exposures using 193 nm immersion lithography:
Wavelength | Refractive index | NA | DOF (normalized)[313] |
---|---|---|---|
193 nm | 1.44 | 1.35 | 1 |
13.3–13.7 nm | 1 | 0.33 | 1.17 |
13.3–13.7 nm | 1 | 0.55 | 0.40 |
High-NA EUV tools also suffer from obscuration, which can cause errors in the imaging of certain patterns.[315]
The first high-NA tools are expected at Intel by 2025 at earliest.[316]
For sub-2nm nodes, high-NA EUV systems will be affected by a host of issues: throughput, new masks, polarization, thinner resists, and secondary electron blur and randomness.[317] Reduced depth of focus requires resist thickness less than 30 nm, which in turn increases stochastic effects, due to reduced photon absorption.
Electron blur is estimated to be at least ~2 nm, which is enough to thwart the benefit of High-NA EUV lithography.[318][319]
Beyond high-NA, ASML in 2024 announced plans for the development of a hyper-NA EUV tool with an NA beyond 0.55, such as an NA of 0.75 or 0.85.[320][321] These machines could cost USD 720 million each and are expected to be available in 2030.[33] A problem with Hyper-NA is polarization of the EUV light causing a reduction in image contrast.[320][322]
Beyond EUV wavelength
[edit]A much shorter wavelength (~6.7 nm) would be beyond EUV, and is often referred to as BEUV (beyond extreme ultraviolet).[323] With current technology, BEUV wavelengths would have worse shot noise effects without ensuring sufficient dose.[324]
References
[edit]- ^ O'Sullivan, Gerry; Li, Bowen; D'Arcy, Rebekah; Dunne, Padraig; Hayden, Paddy; Kilbane, Deirdre; McCormack, Tom; Ohashi, Hayato; O'Reilly, Fergal; Sheridan, Paul; Sokell, Emma; Suzuki, Chihiro; Higashiguchi, Takeshi (2015). "Spectroscopy of highly charged ions and its relevance to EUV and soft x-ray source development". Journal of Physics B: Atomic, Molecular and Optical Physics. 48 (144025): 144025. Bibcode:2015JPhB...48n4025O. doi:10.1088/0953-4075/48/14/144025. S2CID 124221931.
- ^ Bjorkholm, J.; Bokor, J.; Eichner, L.; Freeman, R.; Mansfield, W.; Szeto, L.; Taylor, D.; Tennant, D.; Wood II, O.; Jewell, T.; White, D.; Waskiewicz, W.; Windt, D.; MacDowell, A. (1991). "Soft x-ray projection lithography". Optics and Photonics News. 2 (5): 27. doi:10.1364/OPN.2.5.000027.
- ^ "Making EUV: From lab to fab". 30 March 2022.
- ^ Bakshi, Vivek, ed. (2018). EUV lithography. SPIE PM (Second ed.). Bellingham, Washington, USA: SPIE Press. ISBN 978-1-5106-1679-0.
- ^ "U.S. gives ok to ASML on EUV effort". EE Times. 24 February 1999. Retrieved 17 May 2023.
- ^ "History". ASML.
- ^ "Inside the machine that saved Moore's Law".
- ^ Sascha Migura (2018). "Optics for EUV Lithography" (PDF). euvlitho.com. Retrieved 17 May 2023.
- ^ "The Chip Choke Point TheWire China". 8 February 2021.
- ^ "Extreme Ultraviolet (EUV) Lithography Market Size and Forecast to 2032". PragmaMarketResearch. Retrieved 2024-07-04.
- ^ Anton Shilov (2019-01-28). "ASML to Ship 30 EUV Scanners in 2019: Faster EUV Tools Coming". AnandTech.
- ^ "Overview of EUV Mask Metrology" (PDF). Archived from the original (PDF) on 2017-06-02. Retrieved 2019-06-23.
- ^ a b c d https://www.semiconductor-digest.com/wp-content/uploads/2020/02/SST-Oct-2013.pdf [bare URL PDF]
- ^ Montcalm, C. (March 10, 1998). Multilayer reflective coatings for extreme-ultraviolet lithography. 23. SPIE annual international symposium on microlithography conference, Santa Clara, CA (United States), 22-27 Feb 1998. OSTI 310916.
- ^ Krome, Thorsten; Schmidt, Jonas; Nesládek, Pavel (2018). "EUV capping layer integrity". In Takehisa, Kiwamu (ed.). Photomask Japan 2018: XXV Symposium on Photomask and Next-Generation Lithography Mask Technology. p. 8. doi:10.1117/12.2324670. ISBN 978-1-5106-2201-2. S2CID 139227547.
- ^ US 20030008180A1, Sasa Bajt; James Folta & Eberhard Spiller, "Optimized capping layers for EUV multilayers", published 2003-01-09.
- ^ "Next EUV Issue: Mask 3D Effects". Semiconductor Engineering. April 25, 2018.
- ^ "EUV Mask Blank Battle Brewing". Semiconductor Engineering. November 15, 2018.
- ^ Matsumoto, Hiroshi; Yamaguchi, Keisuke; Kimura, Hayato; Nakayamada, Noriaki (August 23, 2021). "Multi-beam mask writer, MBM-2000". In Ando, Akihiko (ed.). Photomask Japan 2021: XXVII Symposium on Photomask and Next-Generation Lithography Mask Technology. Vol. 11908. SPIE. pp. 175–180. doi:10.1117/12.2604378. ISBN 9781510646858. S2CID 233503067 – via www.spiedigitallibrary.org.
- ^ Waiblinger, M.; Kornilov, K.; Hofmann, T.; Edinger, K. (May 15, 2010). "e-beam induced EUV photomask repair: a perfect match". In Behringer, Uwe F. W.; Maurer, Wilhelm (eds.). 26th European Mask and Lithography Conference. Vol. 7545. SPIE. pp. 243–250. doi:10.1117/12.863542. S2CID 137488152 – via www.spiedigitallibrary.org.
{{cite book}}
:|journal=
ignored (help) - ^ EUV Lithography. SPIE Press. 2009. ISBN 978-0-8194-6964-9.
- ^ Handbook of Photomask Manufacturing Technology. CRC Press. 3 October 2018. ISBN 978-1-4200-2878-2.
- ^ Tomie, Toshihisa (2012-05-21). "Tin laser-produced plasma as the light source for extreme ultraviolet lithography high-volume manufacturing: history, ideal plasma, present status, and prospects". Journal of Micro/Nanolithography, MEMS, and MOEMS. 11 (2): 021109–1. doi:10.1117/1.JMM.11.2.021109. ISSN 1932-5150.
- ^ Elg, Daniel T.; Sporre, John R.; Panici, Gianluca A.; Srivastava, Shailendra N.; Ruzic, David N. (2016). "In situ collector cleaning and extreme ultraviolet reflectivity restoration by hydrogen plasma for extreme ultraviolet sources" (PDF). Journal of Vacuum Science & Technology A. 34 (21305): 021305. Bibcode:2016JVSTA..34b1305E. doi:10.1116/1.4942456.
- ^ Bosgra, Jeroen; Zoethout, Erwin; van der Eerden, Ad M. J.; Verhoeven, Jan; van de Kruijs, Robbert W. E.; Yakshin, Andrey E.; Bijkerk, Fred (2012). "Structural properties of subnanometer thick Y layers in extreme ultraviolet multilayer mirrors". Applied Optics. 51 (36): 8541–8548. Bibcode:2012ApOpt..51.8541B. doi:10.1364/AO.51.008541. PMID 23262592.
- ^ H. Komori et al., Proc. SPIE 5374, pp. 839–846 (2004).
- ^ B. A. M. Hansson et al., Proc. SPIE 4688, pp. 102–109 (2002).
- ^ S. N. Srivastava et al., J. Appl. Phys. 102, 023301 (2007).
- ^ Nigel Farrar; David Brandt; Norbert Böwering (26 February 2009). "OPTICS FOR SCANNING: Multilayer mirrors enable next-generation EUV lithography". Laser Focus World.
- ^ H. S. Kim. "Future of Memory Devices and EUV Lithography" (PDF). 2009 EUV Symposium. Archived from the original (PDF) on 2015-07-10. Retrieved 2012-10-25.
- ^ H. Mizoguchi, "Laser Produced Plasma EUV Light Source Gigaphoton Update", EUVL Source Workshop, May 12, 2008.
- ^ "Behind this Door: Learn about EUV, Intel's Most Precise, Complex Machine". YouTube.
- ^ a b c "Hyper-NA EUV to debut in 2030, primes foundry market for transformation". DIGITIMES. June 28, 2024.
- ^ ASML 2020 Annual Report, p. 68.
- ^ This EUV source has been chosen due to its high CO2 laser to EUV conversion efficiency (~ 5 % or more). See "Igor Fomenkov, EUV Source for Lithography in HVM - performance and prospects, ASML Fellow, Source workshop, Amsterdam, 2019-11-05".
- ^ Yang, De-Kun (2022-07-13). "The development of laser-produced plasma EUV light source". Chip. 1 (3). 100019. doi:10.1016/j.chip.2022.100019.
- ^ "Gigaphoton" (PDF). Archived from the original (PDF) on 9 July 2020. Retrieved 17 May 2023.
- ^ "Cymer SPIE 2018" (PDF).
- ^ "Zeiss 2018 EUVL Workshop update" (PDF).
- ^ "SPIE 2007 paper" (PDF). Archived from the original (PDF) on 2017-08-12. Retrieved 2018-07-28.
- ^ "ASML, 2016 EUVL Workshop, p. 14" (PDF).
- ^ Y. Wang and Y. Liu, Proc. SPIE 9283, 928314 (2014).
- ^ a b c "R. Capelli et al., Proc. SPIE 9231, 923109 (2014)" (PDF). Archived from the original (PDF) on 10 August 2017. Retrieved 17 May 2023.
- ^ "M. van den Brink et al., Proc. SPIE 2726 (1996)" (PDF). Archived from the original (PDF) on 2017-08-09. Retrieved 2018-07-17.
- ^ Schmoeller, Thomas; Klimpel, T.; Kim, I.; Lorusso, G.; Myers, A. F.; Jonckheere, Rik; Goethals, Anne-Marie; Ronse, K. (14 March 2008). "EUV pattern shift compensation strategies". In Schellenberg, Frank M. (ed.). Emerging Lithographic Technologies XII. Proceedings of SPIE. Vol. 6921. pp. 69211B. doi:10.1117/12.772640. S2CID 121926142 – via ResearchGate.
- ^ A. N. Broers, IEEE Trans. Elec. Dev. 28, 1268 (1981).
- ^ Tao, Y.; et al. (2005). "Characterization of density profile of laser-produced Sn plasma for 13.5 nm extreme ultraviolet source". Appl. Phys. Lett. 86 (20): 201501. Bibcode:2005ApPhL..86t1501T. doi:10.1063/1.1931825.
- ^ "Abstract 107 Last Page". www.nifs.ac.jp.
- ^ I. Fomenkov et al., Adv. Opt. Tech. 6, 173 (2017).
- ^ I. V. Fomenkov, Proc. SPIE 10957, 1095719 (2019).
- ^ a b Nadir Faradzhev; Vadim Sidorkin (2009). "Hydrogen mediated transport of Sn to Ru film surface" (PDF). J. Vac. Sci. Technol. A. 27 (2): 306–314. Bibcode:2009JVSTA..27..306F. doi:10.1116/1.3081968. Archived from the original (PDF) on 2016-12-20. Retrieved 2016-12-14.
- ^ a b c Eishi Shiobara (2016-02-16). "Update of Resist Outgas Testing at EIDEC" (PDF). IEUVI Resist TWG, San Jose.
- ^ R. Rokitski et al., Proc. SPIE 7640, 76401Q (2010).
- ^ a b c d M. van de Kerkhof et al., Proc. SPIE 10143, 101430D (2017).
- ^ a b Y. Chen et al., J.Vac. Sci. Tech. B35, 06G601 (2017).
- ^ a b c d e "H. Mizoguchi et al., 2017 EUV-FEL Workshop, p. 4" (PDF).
- ^ "Pinning Down an EUV Resist's Resolution vs. Throughput". www.linkedin.com.
- ^ I. Seshadri et al., IEDM 2023.
- ^ "Assessing EUV Wafer Output: 2019–2022". www.linkedin.com.
- ^ C. Smeets et al., Proc. SPIE 12494, 1249406 (2023).
- ^ Paetzel, R.; et al. (2003). Yen, Anthony (ed.). "Excimer lasers for superhigh NA 193-nm lithography". Proc. SPIE. Optical Microlithography XVI. 5040: 1665. Bibcode:2003SPIE.5040.1665P. doi:10.1117/12.485344. S2CID 18953813.
- ^ Harilal, S. S.; et al. (2006). "Spectral control of emissions from tin doped targets for extreme ultraviolet lithography". J. Phys. D. 39 (3): 484–487. Bibcode:2006JPhD...39..484H. doi:10.1088/0022-3727/39/3/010. S2CID 34621555.
- ^ T. Asayama et al., Proc. SPIE vol. 8683, 86831G (2013).
- ^ "ASML update Nov. 2013, Dublin" (PDF).
- ^ L. Peters, "Double Patterning Leads Race for 32 nm", Semiconductor International, October 18, 2007.
- ^ M. Sugawara et al., J. Vac. Sci. Tech. B 21, 2701 (2003).
- ^ "What is Shadowing in EUV Lithography?". 28 January 2022 – via www.youtube.com.
- ^ a b c Yunfei Deng; Bruno M. La Fontaine; Harry J. Levinson; Andrew R. Neureuther (2003). "Rigorous EM simulation of the influence of the structure of mask patterns on EUVL imaging". In Roxann L. Engelstad (ed.). Emerging Lithographic Technologies VII. Vol. 5037. doi:10.1117/12.484986. S2CID 137035695.
- ^ G. McIntyre et al., Proc. SPIE vol. 7271, 72711C (2009).
- ^ T. Last et al., Proc. SPIE 9985, 99850W (2016).
- ^ a b T. Last et al., Proc. SPIE vol. 10143, 1014311 (2017).
- ^ W. Gao et al., Proc. SPIE vol. 10143, 101430I (2017).
- ^ "Polarization by Reflection in EUV Lithography Systems". 21 August 2022 – via www.youtube.com.
- ^ "The Growing Significance of Polarization in EUV Lithography". www.linkedin.com.
- ^ M. Burkhardt et al., Proc. SPIE 10957, 1095710 (2019).
- ^ A. Erdmann, P. Evanschitzky, T. Fuhrer, Proc. SPIE 7271, 72711E (2009).
- ^ "Double Diffraction Model of EUV Masks". 26 September 2021 – via www.youtube.com.
- ^ "Double Diffraction in EUV Masks: Seeing Through The Illusion of Symmetry". www.linkedin.com.
- ^ "EUV Mask Flatness Requirements" (PDF). Archived from the original (PDF) on 2015-06-26. Retrieved 2015-06-26.
- ^ T. Schmoeller et al., Proc. SPIE vol. 6921, 69211B (2008).
- ^ P. Liu et al., Proc. SPIE vol. 8679, 86790W (2013).
- ^ a b M. Sugawara et al., Proc. SPIE 9048, 90480V (2014).
- ^ a b X. Chen et al., Proc. SPIE 10143, 101431F (2017).
- ^ "TWINSCAN NXE:3400B". ASML. Archived from the original on 2018-12-15. Retrieved 2017-07-02.
- ^ a b X. Liu et al., Proc. SPIE vol. 9048, 90480Q (2014).
- ^ O. Wood et al., Proc. SPIE 10450, 1045008 (2017).
- ^ S. Yoshitake et al., EUV Mask Flatness Requirements: E-beam Mask Writer Supplier Perspective.
- ^ J.-H. Franke et al., Proc. SPIE 11147, 111470E (2019).
- ^ "Defocus Induced Image Shift in EUV Lithography". 24 January 2023 – via www.youtube.com.
- ^ A. Shchegrov et al., Proc. SPIE 11325, 113251P (2020).
- ^ J-H. Franke et al., J. Micro/Nanopatterning, Materials, and Metrology 21, 030501 (2022).
- ^ H. N. Chapman and K. A. Nugent, Proc. SPIE 3767, 225 (1999).
- ^ H. Komatsuda, Proc. SPIE 3997, 765 (2000).
- ^ Q. Mei et al., Proc. SPIE 8679, 867923 (2013).
- ^ D. Hellweg et al., Proc. SPIE 7969, 79690H (2011).
- ^ K. Hooker et al., Proc. SPIE 10446, 1044604 (2017).
- ^ A. Garetto et al., J. Micro/Nanolith. MEMS MOEMS 13, 043006 (2014).
- ^ a b T-S. Eom et al., Proc. SPIE 8679, 86791J (2013).
- ^ R. Capelli et al., Proc. SPIE 10957, 109570X (2019).
- ^ a b J. Fu et al., Proc. SPIE 11323, 113232H (2020).
- ^ Miyakawa, R.; Naulleau, P. (May 13, 2019). "Preparing for the Next Generation of EUV Lithography at the Center for X-ray Optics". Synchrotron Radiation News. 32 (4): 15–21. Bibcode:2019SRNew..32...15M. doi:10.1080/08940886.2019.1634432. OSTI 1582044. S2CID 202145457 – via escholarship.org.
- ^ S. Koo et al., Proc. SPIE 7969, 79691N (2011).
- ^ US Patent Application 20070030948.
- ^ "M. F. Bal et al., Appl. Opt. 42, 2301 (2003)" (PDF).
- ^ D. M. Williamson, Proc. SPIE 3482, 369 (1998).
- ^ a b "Carl Zeiss 2018" (PDF).
- ^ a b M. Lim et al., Proc. SPIE 10583, 105830X (2018).
- ^ A. V. Pret et al., Proc. SPIE 10809, 108090A (2018).
- ^ L. van Look et al., Proc. SPIE 10809, 108090M (2018)
- ^ R-H. Kim et al., Proc. SPIE 9776, 97761R (2016).
- ^ a b c E. van Setten et al., Proc. SPIE 9661, 96610G (2015).
- ^ T. E. Brist and G. E. Bailey, Proc. SPIE 5042, 153 (2003).
- ^ G. Zhang et al., Proc. SPIE 5040, 45 (2003).
- ^ "Resolution vs. Die Size Tradeoff Due to EUV Pupil Rotation". www.linkedin.com.
- ^ a b "Horizontal, Vertical, and Slanted Line Shadowing Across Slit in Low-NA and High-NA EUV Lithography Systems". www.linkedin.com.
- ^ K. Lee et al., J. Microlith/Nanolith. MEMS MOEMS 18, 040501 (2019).
- ^ K. A. Goldberg et al., Proc. SPIE 5900, 59000G (2005).
- ^ Y. Liu and Y. Li, Opt. Eng. 55, 095108 (2016).
- ^ a b R., Saathof (1 December 2018). Adaptive Optics to Counteract Thermal Aberrations: System Design for EUV-Lithography with Sub-nm Precision (Doctoral thesis). Technische Universiteit Delft. doi:10.4233/uuid:1d71e3e8-88ce-4260-aeda-af0ee7675445.
- ^ T. S. Jota and R. A. Chipman, Proc. SPIE 9776, 977617 (2016).
- ^ a b c "Mentor Graphics Director Details Challenges for Edge Placement Control in 2020". nikonereview.com. Archived from the original on 2018-12-01. Retrieved 2017-10-24.
- ^ M. Habets et al., Proc. SPIE 9776, 97762D (2016).
- ^ M. Bayraktar et al., Opt. Exp. 22, 30623 (2014).
- ^ "Nonideal Imaging in EUV Lithography Systems". 11 September 2021 – via www.youtube.com.
- ^ George, Simi A.; Nauleau, Patrick; Rekawa, Senajith; Gullikson, Eric; Kemp, Charles D. (February 23, 2009). Schellenberg, Frank M; La Fontaine, Bruno M (eds.). "Out-of-band exposure characterization with the SEMATECH Berkeley 0.3-NA microfield exposure tool". Journal of Micro/Nanolithography, MEMS, and MOEMS. Alternative Lithographic Technologies. 7271: 72710X. Bibcode:2009SPIE.7271E..0XG. doi:10.1117/12.814429. OSTI 960237. S2CID 55241073.
- ^ a b c d "Measurement and characterization of EUV mask performance at high-NA | EECS at UC Berkeley". www2.eecs.berkeley.edu.
- ^ "Carl Zeiss SMT GMbH, Semicon Europa, Nov. 16 2018" (PDF). Archived from the original (PDF) on 19 June 2020. Retrieved 17 May 2023.
- ^ a b "Multilayer Reflectivity". henke.lbl.gov.
- ^ Y. Nakajima et al., Proc. SPIE 7379, 73790P (2009).
- ^ a b N. Davydova et al., Proc. SPIE 8166, 816624 (2011).
- ^ G. J. Stagaman et al., Proc. SPIE 2726, 146 (1996).
- ^ M.F. Ravet et al., Proc. SPIE 5250, 99 (2004).
- ^ F. Scholze et al., Proc. SPIE 6151, 615137 (2006).
- ^ Yakshin, A. E.; Kozhevnikov, I. V.; Zoethout, E.; Louis, E.; Bijkerk, F. (2010). "[PDF] Properties of broadband depth-graded multilayer mirrors for EUV optical systems. | Semantic Scholar". Optics Express. 18 (7): 6957–71. doi:10.1364/OE.18.006957. PMID 20389715. S2CID 16163302.
- ^ M. Sugawara et al., J. Micro/Nanolith. MEMS MOEMS 2, 27–33 (2003).
- ^ "OPG | PDF no longer available". opg.optica.org.
- ^ C. S. Choi et al., Proc. SPIE 9235, 92351R (2014).
- ^ Fundamental Principles of Optical Lithography Chris A. Mack, p. 37.
- ^ C. A. Mack, Microlith. World, 9–4, 25 (2000)
- ^ J. S. Petersen et al., Proc. SPIE 3546, 288 (1998).
- ^ "Optical and Physical Characteristics of EUV Phase Shift Masks" (PDF). Archived from the original (PDF) on 2017-02-05. Retrieved 2017-02-05.
- ^ Thin Half-tone Phase Shift Mask Stack for Extreme Ultraviolet Lithography Inhwan Lee, Sangsul Lee, Jae Uk Lee, Chang Young Jeong2, Sunyoung Koo, Changmoon Lim, and Jinho Ahn
- ^ L. Yuan et al., Proc. SPIE 8322, 832229 (2012).
- ^ a b E. van Setten et al., Intl. Symp. on EUV Lithography, 2014.
- ^ V. M. Blanco Carballo et al., Proc. SPIE 10143, 1014318 (2017).
- ^ E. van Setten et al., Proc. SPIE 9231, 923108 (2014).
- ^ F. Jiang et al., Proc. SPIE vol. 9422, 94220U (2015).
- ^ a b c d I. Mochi et al., Proc. SPIE 9776, 97761S (2015).
- ^ J. G. Garofalo et al., Proc. SPIE 2440, 302 (1995).
- ^ "Understanding EUV Shot Noise".
- ^ D. Civay et al., Proc. SPIE 9048, 90483D (2014).
- ^ A.Burov et al., Proc. SPIE 11518, 115180Y (2020).
- ^ A-Y. Je et al., Proc. SPIE 7823, 78230Z (2010).
- ^ T. Huynh-Bao et al., Proc. SPIE 9781, 978102 (2016).
- ^ V. Philipsen et al., Proc. SPIE 9235, 92350J (2014).
- ^ a b W. Gillijns et al., Proc. SPIE 10143, 1014314 (2017).
- ^ a b Y-G Wang et al., Proc. SPIE 10143, 1014320 (2017).
- ^ US Patent 9715170.
- ^ S. Nagahara et al., Proc. SPIE 7640, 76401H (2010).
- ^ L. Pang et al., Proc. SPIE 7520, 75200X (2009).
- ^ Hsu, Stephen D.; Liu, Jingjing (1 January 2017). "Challenges of anamorphic high-NA lithography and mask making". Advanced Optical Technologies. 6 (3–4): 293. Bibcode:2017AdOT....6..293H. doi:10.1515/aot-2017-0024. S2CID 67056068.
- ^ Zhang, Zinan; Li, Sikun; Wang, Xiangzhao; Cheng, Wei; Qi, Yuejing (2021). "Source mask optimization for extreme-ultraviolet lithography based on thick mask model and social learning particle swarm optimization algorithm". Optics Express. 29 (4): 5448–5465. Bibcode:2021OExpr..29.5448Z. doi:10.1364/OE.418242. PMID 33726081. S2CID 232263498.
- ^ "IMEC EUVL 2018 Workshop" (PDF).
- ^ C. Krautschik et al., Proc. SPIE 4343, 392 (2001).
- ^ A. Erdmann, P. Evanschitzky, and T. Fuhner, Proc. SPIE 7271, 72711E (2009).
- ^ A. Erdmann et al., J. Micro/Nanolith. MEMS MOEMS 15, 021205 (2016).
- ^ M. Burkhardt and A. Raghunathan, Proc. SPIE 9422, 94220X (2015).
- ^ Z. Zhu et al., Proc. SPIE 5037, 494 (2003)
- ^ V. Philipsen et al., Proc. SPIE 10143, 1014310 (2017).
- ^ Naulleau, Patrick P.; Rammeloo, Clemens; Cain, Jason P.; Dean, Kim; Denham, Paul; Goldberg, Kenneth A.; Hoef, Brian; La Fontaine, Bruno; Pawloski, Adam R.; Larson, Carl; Wallraff, Greg (2006). Lercel, Michael J (ed.). "Investigation of the Current Resolution Limits of Advanced Extreme Ultraviolet (EUV) Resists". Emerging Lithographic Technologies X. 6151: 289. Bibcode:2006SPIE.6151..289N. CiteSeerX 10.1.1.215.7131. doi:10.1117/12.657005. S2CID 97250792.
- ^ A. Erdmann et al., J. Micro/Nanolith. MEMS MOEMS 15(2), 021205 (2016).
- ^ J. Finders et al., Proc. SPIE 9776, 97761P (2016).
- ^ D. Rio et al, Proc. SPIE 10809, 108090N (2018).
- ^ C-H. Chang et al., Proc. SPIE 5377, 902 (2004).
- ^ T. Devoivre et al., MTDT 2002.
- ^ L. C. Choo et al., Proc. SPIE vol. 4000, 1193 (2000).
- ^ J. Word and K. Sakajiri, Proc. SPIE 6156, 61561I (2006).
- ^ T. Winkler et al., Prod. SPIE 5754, 1169 (2004).
- ^ Y. Borodovsky et al., Proc. SPIE 4754, 1 (2002).
- ^ S-S. Yu et al., Proc. SPIE 8679, 86791L (2013).
- ^ a b A. Erdmann et al., Proc. SPIE 10583, 1058312 (2018).
- ^ "Phase-Shifting Masks for NILS Improvement - A Handicap For EUV?". www.linkedin.com.
- ^ "Eigenmode analysis of EM fields in EUV masks" (PDF).
- ^ "Ultra-high efficiency EUV etched phase-shift mask" (PDF).
- ^ Naulleau, P., Anderson, C.N., Baclea-an, L.M., Chan, D., Denham, P., George, S., Goldberg, K.A., Hoef, B., Jones, G., Koh, C. and La Fontaine, B., 2010, March. The SEMATECH Berkeley MET pushing EUV development beyond 22nm half pitch. In Extreme Ultraviolet (EUV) Lithography (Vol. 7636, pp. 530-538). SPIE.
- ^ ". Torok et al., "Secondary Electrons in EUV Lithography", J. Photopol. Sci. and Tech., 26, 625 (2013)".
- ^ K. Ishii and T. Matsuda, Jpn. J. Appl. Phys. 29, 2212 (1990).
- ^ A. Thete et al., Proc. SPIE 9422, 94220A (2015).
- ^ "B. Sun thesis, p. 34" (PDF).
- ^ "S. Bhattarai, Study of Line Edge Roughness and Interactions of Secondary Electrons in Photoresists for EUV Lithography, 2017, p. 100" (PDF). Archived from the original (PDF) on 2017-10-21. Retrieved 2018-09-16.
- ^ D. D. Simone et al., Proc. SPIE 10143, 101430R (2017).
- ^ "Defocus Impact on Electron Blur in EUV Lithography". 4 March 2023 – via www.youtube.com.
- ^ M.I.Jacobs et al., Phys. Chem. Chem. Phys. 19(20) (2017).
- ^ P. Theofanis et al., Proc. SPIE 11323, 113230I (2020).
- ^ "Electron Blur Impact in EUV Resist Films from Interface Reflection". www.linkedin.com.
- ^ O. Yu et al., J. Elec. Spec. and Rel. Phenom. 241, 146824 (2020).
- ^ N. Miyahara et al., Proc. SPIE 12498, 124981E (2023)
- ^ Defocus Aggravates Stochastic EUV Images
- ^ J. Hollenshead and L. Klebanoff, J. Vac. Sci. & Tech. B 24, pp. 118–130 (2006).
- ^ G. Denbeaux et al., 2007 European Mask and Lithography Conference.
- ^ I. Pollentier et al., Proc. SPIE vol. 7972, 797208 (2011).
- ^ G. Denbeaux, 2009 Intl. Workshop on EUV Lithography.
- ^ J. Y. Park et al., J. Vac. Sci. Tech. B29, 041602 (2011).
- ^ a b c d e Crijns, V. M. C. (2014). "Hydrogen atom based tin cleaning" (PDF). Eindhoven University of Technology.
- ^ a b T. Van de Ven et al., J. Appl. Phys. 123, 063301 (2018).
- ^ Computer modeling of contamination and cleaning of EUV source optics. RnD-ISAN/EUV Labs & ISTEQ BV.
- ^ The Denitridation of Nitrides Under Hydrogen.
- ^ "C. G. van de Walle and B. Tuttle, THEORY OF HYDROGEN INTERACTIONS WITH AMORPHOUS SILICON in Amorphous and Heterogeneous Silicon Thin Films — Fundamentals to Devices, edited by H. M. Branz, R. W. Collins, H. Okamoto, S. Guha, and B. Schropp, MRS Symposia Proceedings, Vol. 557 (MRS, Pittsburgh, Pennsylvania, 1999), p. 255" (PDF).
- ^ T. Tanabe, Y. Yamanishi, and S. Imoto, J. Nucl. Mat. 191–194, 439 (1992).
- ^ a b "Hydrogen Blistering in EUV Multilayers". 6 October 2022 – via www.youtube.com.
- ^ a b "D. T. Elg et al., J. Vac. Sci. Tech. A 34, 021305 (2016)" (PDF).
- ^ "Hydrogen-induced blistering in thin film multilayers" (PDF).
- ^ I-Y. Jang et al., Proc. SPIE 9256, 92560I (2014)
- ^ "Hydrogen penetration of Ru and Pd/Ru" (PDF).
- ^ Pantisano, L; Schram, Tom; Li, Z; Lisoni, Judit; Pourtois, Geoffrey; De Gendt, Stefan; P. Brunco, D; Akheyar, A; Afanas'ev, V.V.; Shamuilia, Sheron; Stesmans, A (12 June 2006). "Ruthenium gate electrodes on SiO2 and HfO2: Sensitivity to hydrogen and oxygen ambients". Applied Physics Letters. 88 (24): 243514. Bibcode:2006ApPhL..88x3514P. doi:10.1063/1.2212288 – via ResearchGate.
- ^ "Hydrogen penetration of boron carbide".
- ^ M. Mayer, M. Balden, and R. Behrisch, J. Nucl. Mat. 252, 55 (1998).
- ^ a b S-S. Kim et al., Proc. SPIE 10143, 1014306 (2017).
- ^ "Screening of oxidation-resistance capping layers" (PDF).
- ^ B. Thedjoisworo et al., J. Vac. Sci. Tech. A 30, 031303 (2012).
- ^ "Hydrogen plasma for photoresist stripping" (PDF). Archived from the original (PDF) on 2020-03-21. Retrieved 2019-01-06.
- ^ "Metal Oxide Resist Outgassing" (PDF).
- ^ Thedjoisworo, Bayu; Cheung, David; Crist, Vince (2013). "Comparison of the effects of downstream H2- and O2-based plasmas on the removal of photoresist, silicon, and silicon nitride". Journal of Vacuum Science & Technology B, Nanotechnology and Microelectronics: Materials, Processing, Measurement, and Phenomena. 31 (2): 021206. Bibcode:2013JVSTB..31b1206T. doi:10.1116/1.4792254. ISSN 2166-2746.
- ^ J. Beckers et al., Appl. Sci. 9,2827 (2019).
- ^ P. De Schepper et al., J. Micro/Nanolith. MEMS MOEMS 13, 023006 (2014).
- ^ a b E-S. Choe et al., Adv. Mater. Interfaces 2023, 2300867.
- ^ P. De Schepper et al., Proc. SPIE 9428, 94280C (2015).
- ^ Huang, Y. H.; Lin, C. J.; King, Y. C. (2023). "A study of hydrogen plasma-induced charging effect in EUV lithography systems". Discover Nano. 18 (1): 22. Bibcode:2023NRL....18...22H. doi:10.1186/s11671-023-03799-4. PMC 9950305. PMID 36823307.
- ^ M. van de Kerkhof et al., Rad. Effects and Defects in Solids, 177, 486 (2022).
- ^ K. Bystrov et al., J. Vac. Sci. Tech. A 31, 011303 (2013).
- ^ Nanoparticles in the EUV-Induced Plasma: Another Possible Origin for Stochastic Defects in EUV Lithography
- ^ Nanoparticles in the EUV-Induced Plasma: Another Possible Origin for Stochastic Defects
- ^ "Getting up to speed with roadmap requirements for extreme-UV lithography". spie.org.
- ^ "Fast Simulation Methods for Non-Planar Phase and Multilayer Defects in DUV and EUV Photomasks for Lithography". berkeley.edu.
- ^ H. Yu et al., J. Vac. Sci. Tech. A31, 021403 (2013).
- ^ S. Huh et al., Proc. SPIE 7271 (2009).
- ^ K. Seki et al., Proc. SPIE 9658, 96580G (2015).
- ^ A. Garetto et al., J. Micro/Nanolith. MEMS MOEMS 13, 043006 (2014).
- ^ a b Y. Chen et al., Proc. SPIE 10143, 101431S (2017).
- ^ R. Jonckheere and L. S. Melvin III, Proc. SPIE 11517, 1151710 (2020).
- ^ M. Muller et al., Appl. Phys. A vol. 108, 263 (2012).
- ^ "EUVL activities in South Korea (including Samsung and SKHynix)" (PDF).
- ^ I-S. Kim et al., Proc. SPIE vol. 8322, 83222X (2012).
- ^ C. Zoldeski et al., Proc. SPIE vol. 9048, 90481N (2014).
- ^ D. L. Goldfarb, Dec. 2015 BACUS Newsletter.
- ^ "EUV Pellicle, Uptime And Resist Issues Continue". 26 September 2018.
- ^ A. Gao et al., J. Appl. Phys. 114, 044313 (2013).
- ^ E. Gallagher et al., Proc. SPIE vol. 9635, 96350X (2015).
- ^ C. Ghica et al., Rom. Rep. in Phys., vol. 62, 329–340 (2010).
- ^ L. Juan et al., Chin. Phys. B, vol., 22, 105101 (2013).
- ^ I. Pollentier et al., Proc. SPIE vol. 10143, 101430L (2017).
- ^ I-S. Kim et al., Microel. Eng. 177, 35 (2017).
- ^ a b H. J. Levinson and T. A. Brunner, Proc. SPIE 10809, 1080903 (2018).
- ^ "TSMC Manufacturing Update: N6 to Match N7 Output by EOY, N5 Ramping Faster, Better Yields Than N7".
- ^ "Samsung to develop 'Pellicle', an essential EUV process product - ETNews". 13 October 2021.
- ^ a b US Patent 12025922
- ^ a b P. De Bisschop, "Stochastic effects in EUV lithography: random, local CD variability, and printing failures", J. Micro/Nanolith. MEMS MOEMS 16(4), 041013 (2017).
- ^ Visualizing EUV Stochastics for a 14nm DRAM Example
- ^ a b c d e P. De Bisschop and E. Hendrickx, Proc. SPIE 10583, 105831K (2018).
- ^ EUV Stochastic Variability in Line Cuts
- ^ The Stochastic Impact of Defocus in EUV Lithography
- ^ The Stochastic Impact of Defocus in EUV Lithography
- ^ a b A. Narasimhan et al., Proc. SPIE 9422, 942208 (2015).
- ^ Fukuda, Hiroshi (February 23, 2019). "Localized and cascading secondary electron generation as causes of stochastic defects in extreme ultraviolet projection lithography". Journal of Micro/Nanolithography, MEMS, and MOEMS. 18 (1): 013503. Bibcode:2019JMM&M..18a3503F. doi:10.1117/1.JMM.18.1.013503.
- ^ L. Meli et al., J. Micro/Nanolith. MEMS MOEMS 18, 011006 (2019).
- ^ N. Felix et al., Proc. SPIE 9776, 97761O (2015).
- ^ "S. Bhattarai, PhD Thesis,"Study of Line Edge Roughness and Interactions of Secondary Electrons in Photoresists for EUV Lithography," U. Calif. Berkeley, 2017" (PDF).
- ^ S. Larivière et al., Proc. SPIE 10583, 105830U (2018).
- ^ J. Kim et al., Proc. SPIE 11328, 113280I (2020).
- ^ S. M. Kim et al., Proc. SPIE 9048, 90480A (2014).
- ^ S. Das et al., Proc. SPIE 10959, 109590H (2019).
- ^ a b c H-W Kim et al., Proc. SPIE 7636, 76360Q (2010).
- ^ S-M. Kim et al., Proc. SPIE 9422, 94220M (2015).
- ^ B. Baylav, "Reduction of Line Edge Roughness (LER) in Interference-Like Large Field Lithography", PhD dissertation, p. 37, 2014.
- ^ Z-Y. Pan et al., Proc. SPIE 6924, 69241K (2008).
- ^ "2013 Nissan Chemical Industries, 2013 International Workshop on EUV Lithography" (PDF).
- ^ T. G. Oyama et al., Appl. Phys. Exp. 7, 036501 (2014).
- ^ T. Kozawa, Jpn. J. Appl. Phys. 51, 06FC01 (2012).
- ^ EUV Resist Absorption Impact on Stochastic Defects
- ^ IRDS 2022 Lithography Roadmap
- ^ Y. J. Choi et al., “Stochastic defect removal coating for high-performance extreme ultraviolet lithography,” J. Vac. Sci. Tech. B 40, 042602 (2022).
- ^ Y. Li, Q. Wu, Y. Zhao, “A Simulation Study for Typical Design Rule Patterns and Stochastic Printing Failures in a 5 nm Logic Process with EUV Lithography,” CSTIC 2020.
- ^ T-T. Wu et al., Proc. SPIE 12955, 129552V (2024).
- ^ a b R. Socha, Proc. SPIE 11328, 113280V (2020).
- ^ B. Sell et al., VLSI Tech. 2022]
- ^ J-H. Franke et al., Proc. SPIE 11517, 1151716 (2020).
- ^ The Tradeoff of EUV Numerical Aperture: Depth-of-Focus vs. Pupil Fill.
- ^ W. Gap et al., Proc. SPIE 10583, 105830O (2018).
- ^ D. De Simone et al., Advanced Lithography 2019, 10957-21.
- ^ "Samsung 18 nm DRAM cell integration: QPT and higher uniformed capacitor high-k dielectrics". techinsights.com.
- ^ Roos, Gina (May 24, 2018). "Prices for DRAMs Continue to Climb while NAND Flash ASPs Drop".
- ^ "SemiWiki.com - Top 10 Highlights from the TSMC Open Innovation Platform Ecosystem Forum". www.semiwiki.com. 7 August 2023.
- ^ "DAC 2018 TSMC/Arm/Synopsys Breakfast". www.synopsys.com. Archived from the original on 2018-10-05. Retrieved 2018-10-05.
- ^ "Cadence Achieves EDA Certification for TSMC 5nm and 7nm+ FinFET Process Technologies to Facilitate Mobile and HPC Design Creation" (Press release). October 2018.
- ^ "Synopsys Digital and Custom Design Platforms Certified on TSMC 5-nm EUV-based Process Technology". Design And Reuse.
- ^ "DAC 2018 Samsung/Synopsys Breakfast". www.synopsys.com. Archived from the original on 2018-10-05. Retrieved 2018-10-05.
- ^ Merritt, Rick. "TSMC Goes Photon to Cloud". EETimes.
- ^ "Intel presentation on Complementary Lithography at 2012 International Workshop on EUV Lithography" (PDF).
- ^ a b c "EUV was never going to be single patterning". 5 February 2017.
- ^ S. Hsu et al., Proc. SPIE 4691, 476 (2002).
- ^ X. Liu et al., Proc. SPIE 9048, 90480Q (2014).
- ^ S-Y. Oh et al., Proc. SPIE 4691, 1537 (2002).
- ^ D. Rio et al., Proc. SPIE 10809, 108090N (2018).
- ^ W. Gao et al., Proc. SPIE 11323, 113231L (2020).
- ^ R. K. Ali et al., Proc. SPIE 10583, 1058321 (2018).
- ^ Q. Lin, Proc. SPIE 11327, 113270X (2020).
- ^ R. Venkatesan et al., Proc. SPIE 12292, 1229202 (2022).
- ^ J. T. Neumann et al., Proc. SPIE 8522, 852211 (2012).
- ^ Intel's Xeon E5-2600 V4 Chips Feature An Insane 7.2 Billion Transistors on a 456mm2 Die,
- ^ J. van Schoot et al., Proc. SPIE 9422, 94221F (2015).
- ^ B. J. Lin, JM3 1, 7–12 (2002).
- ^ E. R. Hosler et al., Proc. SPIE vol. 9776, 977616 (2015).
- ^ a b B. J. Lin, J. Microlith., Microfab., Microsyst. 1, 7–12 (2002).
- ^ B. J. Lin, Microelec. Eng. 143, 91–101 (2015).
- ^ B. Bilski et al., Proc. SPIE 11177, 111770I (2019).
- ^ Intel roadmap
- ^ Reality Checks for High-NA EUV for 1.x nm Nodes
- ^ L. F. Miguez et al., Proc. SPIE 12498, 124980E (2023).
- ^ R. Fallica et al., Proc. SPIE 12498, 124980J (2023).
- ^ a b "ASML Aims for Hyper-NA EUV, Shrinking Chip Limits". 12 June 2024.
- ^ biz.chosun.com/it-science/ict/2024/06/21/OTIF4YUEGZCSLNPMHY53HH34DQ/
- ^ Lee, Inhwan; Franke, Joern-Holger; Philipsen, Vicky; Ronse, Kurt; De Gendt, Stefan; Hendrickx, Eric (2023). "Hyper-NA EUV lithography: An imaging perspective". Optical and Euv Nanolithography Xxxvi. 12494. Bibcode:2023SPIE12494E..05L. doi:10.1117/12.2659153.
- ^ "ASML presentation at 2010 International Workshop on Extreme Ultraviolet Sources" (PDF).
- ^ Mojarad, Nassir; Gobrecht, Jens; Ekinci, Yasin (18 March 2015). "Beyond EUV lithography: a comparative study of efficient photoresists' performance". Scientific Reports. 5 (1): 9235. Bibcode:2015NatSR...5E9235M. doi:10.1038/srep09235. PMC 4363827. PMID 25783209.
Further reading
[edit]- Banqiu Wu and Ajay Kumar (May 2009). Extreme Ultraviolet Lithography. McGraw-Hill Professional, Inc. ISBN 978-0-07-154918-9.
- Banqiu Wu and Ajay Kumar (2009). "Extreme Ultraviolet Lithography: Towards the Next Generation of Integrated Circuits". Optics & Photonics Focus. 7 (4).
- Michael Purvis, An Introduction to EUV Sources for Lithography, ASML, STROBE, 2020-09-25.
- Igor Fomenkov, EUV Source for Lithography in HVM - performance and prospects, ASML Fellow, Source workshop, Amsterdam, 2019-11-05.